摘要
在1060系铝基体表面镀镍碳纤维作为增强体,进行真空热压扩散制备出碳纤维/铝复层材料。研究了制备工艺参数(加热温度、保温时间、压力大小)和碳纤维体积分数对碳纤维/铝复层材料的微观组织、界面结合、性能强度和断口形貌的影响。结果表明:碳纤维与铝基体界面结合良好,镀镍层与铝基体在碳纤维附近反应生成的AlNi阻止了铝基体与碳纤维之间生成脆性相AlC。随着碳纤维体积分数的提高,材料的抗弯强度先提高后降低。
Carbon fibre-reinforced aluminium laminates was prepared by vacuum hot pressing diffusion with 1060 series aluminum as matrix and nickel plated carbon fiber as reinforcement in this paper.The effects of preparation parameters(heating temperature, holding time, pressure) and carbon fiber volume fraction on the microstructure, interfacial bonding, mechanical strength and fracture morphology of Carbon fibre-reinforced aluminium laminates were investigated. The results show that the interface between carbon fiber and aluminum matrix is well bonded, and the nickel coating and aluminum matrix react near the carbon fiber to form AlNi, which effectively prevents the formation of brittle phase AlC between aluminum matrix and carbon fiber. With the increase of carbon fiber volume fraction, the bending strength first increases and then decreases.
作者
王艳坤
王宇
纪伟
王智慧
彭翔飞
呼宇雄
刘斌
徐宏
白培康
WANG Yankun;WANG Yu;JI Wei;WANG Zhihui;PENG Xiangfei;HU Yuxiong;LIU Bin;XU Hong;BAI Peikang(School of materials science and engineering,North University of China,Taiyuan 030000,China;Inner Mongolia Metal Material Research Institute,Yantai 264000,China)
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2022年第7期536-544,共9页
Chinese Journal of Materials Research
基金
山西省面上青年基金(201801D221148)
山西省高等学校科技创新项目(2020L0319)
国防科工局稳定支持经费专项-兵器五五所开放创新项目(JB11-12)
安徽省重点研究与开发计划(202004A05020070)
山西省重点研发计划国际科技合作项目(201903D421080)。
关键词
复合材料
碳纤维/铝复层材料
三点弯曲
制备工艺
界面微观结构
composites
carbon fiber/aluminum laminated composites
three point bending
fabrication process
interface microstructure