摘要
The deformation twins initiated in CrMnFeCoNi high entropy alloy at cryogenic temperature are experimentally studied. Under the external loading, a three-dimensional shear stress concentration originating from dislocation tangling at both the grain boundaries and twin boundaries could be formed, which promotes emission of partial dislocations from the planar defects and is thus considered to be the key factor for twin formation. A sympathetic nucleation mechanism is proposed to describe the nucleation behaviors of twins.
基金
supported by the National Natural Science Foundation of China(Nos.51872159 and 51572145)。