摘要
Semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys were prepared by semi-solid isothermal heat treatment.The effects of the La element on the as-cast and semi-solid microstructures of Mg-7Zn alloy were investigated.Meanwhile,the effects of isothermal temperature and holding time on the evolution of the semi-solid microstructure of Mg-7Zn-0.3La alloy were also studied.Results indicate that the addition of a small amount of La can significantly refine the as-cast and semi-solid microstructure.During the semi-solid thermal transformation,the size and shape factor of solid particles decrease at first and then increase with the increase of isothermal temperature and holding time.The semi-solid microstructure of Mg-7Zn-0.3La alloy obtained by holding at 605℃ for 30 min is the optimal.The average size of solid particles,shape factor,and solid fraction are 42μm,1.45 and 61.8%,respectively.At the same time,a comparative study on the coarsening process of particles in the semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys reveals that the addition of La effectively decreases the coarsening rate of solid particles and restricts the growth of solid particles.
基金
financially supported by the National Natural Science Foundation of China (Grant No. 51464032)