Al_(2)O_(3)-SiO_(2) based gunning mixes were prepared with electric porcelain waste,silica fume,bauxite,quartz powder,and calcium aluminate cement(CAC)of different additions as raw materials firing at different temperatures to research the effect of the CAC addition on their phase change and properties.The results show that:from theoretical analysis of the phase diagram,with the CAC addition increasing from 8%to 14%,anorthite increases from 40.0%to 77.7%,by mass.With the rising CAC addition,the permanent linear change on heating of specimens increases;for the specimens dried at 110℃or hot-treated at 1000℃,the bulk density and the mechanical properties increase,and the apparent porosity decreases;and for those hottreated at 1300℃,the bulk density and the mechanical properties firstly increase,and then decrease,while the apparent porosity shows an opposite trend.Taking into account the phases at high temperatures and the properties,the optimal CAC addition of Al_(2)O_(3)-SiO_(2) based gunning mixes is 12%.