摘要
采用≥40%铁水-50 t EAF-LF-VD-180 mm×220 mm铸坯-轧制流程开发了45Mn2R钢Φ40~50 mm轧材。通过控制EAF终点[C]≥0.10%,[P]≤0.015%,出钢温度1620~1660℃,出钢过程用“增碳剂+复合脱氧剂(15%Ca-12%Al-45%Si)+合成渣(50%CaO-34%Al_(2)O_(3)-4%MgO)”预脱氧,Ca处理前钢水S含量≤0.010%,Ca处理20 min后喂S线,VD后软吹25~30 min等工艺措施,提升钢的纯净度和可浇性。结果表明,生产的45Mn2R钢(/%:0.43~0.46C,0.22~0.27Si,0.009~0.017P,0.065~0.086S,0.32~0.36Cr,0.003~0.010Ti,0.013~0.034Als)具有良好的综合性能,各项指标满足用户要求。
The 45Mn2R steelΦ40~50 mm rolled product is developed by≥40%hot metal-50 t EAF-LF-VD-180 mm×220 mm cast billet-rolling flow sheet.The cleanliness and casting ability are improved by controlling EAF end[C]≥0.10%,[P]≤0.015%,tapping temperature 1620~1660℃,preliminay deoxidation using"recaburizing agent+(15%Ca-12%Al-45%Si)compound deoxidation reagent+(50%CaO-34%Al_(2)O_(3)-4%MgO)synthetic slag"during tapping,S content in metal≤0.010%before Ca treatment,feeding S wire after Ca treatment for 20 min,soft blowing for 20 min after VD etc process measure.Results show that produced 45Mn2R steel(/%:0.43~0.46C,0.22~0.27Si,0.009~0.017P,0.065~0.086S,0.32~0.36Cr,0.003~0.010Ti,0.013~0.034Als)has better comprehensive properties to meet user requirement.
作者
梁娜
刘永昌
王升
Liang Na;Liu Yongchang;Wang Sheng(Shandong Iron and Steel Company Ltd.,Laiwu 271105)
出处
《特殊钢》
2022年第5期51-54,共4页
Special Steel