摘要
This study assessed the usefulness of the replacement of coarse aggregate partially with electronic waste(e-waste)plastic in lightweight concrete since developing countries have been challenged with management of e-waste as well as high cost of coarse aggregates for concrete production.Coarse aggregates were replaced with e-waste plastic in concrete at 5%,10%,15%,and 20% for a concrete class of C20.The particle size distribution of the e-waste plastic aggregates was determined as well as the slump,compressive strength,water absorption and bulk density of the concrete.Generally,the slump decreased as the e-waste increased.The compressive strengths decreased for the 5%and 10%replacement of coarse aggregates with e-waste but increased for the 15% and 20% replacement of coarse aggregate with e-waste.0% water absorption was obtained for the 15% and 20% e-waste content while the 10%e-waste concrete obtained 0.01% and the 5% e-waste obtaining of 0.013% after 28days of curing.The densities of 5%,10%,15% and 20% e-waste plastic content decreased as compared to the 0% e-waste plastic content.The values of compressive strength obtained showed that coarse aggregate replacements by e-waste plastic at 15% and 20% may be appropriate for lightweight concrete of class C20/25 since compressive strengths ranged between 16.09 Nmm^(-2) and 22.87 Nmm^(-2).This implies that partial replacement of coarse aggregate with e-waste plastic may be useful for lightweight concrete as well as helping in eradicating the environment of the menace of e-waste plastic.