Temperature dependent behaviors of electro-elastic properties of NdCa_(4)O(BO_(3))_(3)crystal with monoclinic symmetry

Rare-earth calcium oxyborate crystals(RECa_(4)O(BO_(3))_(3),RECOB,RE:rare-earth elements)are a kind of multifunctional crystal materials.In this work,the temperature dependent behaviors of the electroelastic constants of NdCOB crystal were investigated over the temperature range of-80-200℃,and their temperature coefficients were evaluated.It is found that NdCOB crystal possesses minimal variation of relative dielectric permittivities(<3%).The temperature coefficient of frequency for ZY cut with width shear vibration mode is in the order of 0.07×10^(-4)/℃.The temperature coefficients of the elastic compliances are obtained to be in the range of-33.0×10^(-4)/℃-32.2×10^(-4)/℃.Particularly,the sand swere found to show low temperature coefficients of the elastic compliances,i.e.1.0×10^(-4)/℃and-0.4×10^(-4)/℃,respectively,indicating the existence of zero temperature coefficient of frequency crystal cut.Furthermore,the electromechanical coupling factors and piezoelectric coefficients as a function of temperature were studied.The electromechanical coupling factor kand piezoelectric coefficient dare determined to be~30.8%and~15.2 pC/N at room temperature,respectively.The large piezoelectric response and zero temperature coefficient of frequency indicate the potential usage of NdCOB crystal for piezoelectric frequency devices over a wide temperature range.