采用矿渣制备了超硫酸盐水泥,研究了硫酸亚铁和硝酸钙的掺量和掺加方式对超硫酸盐水泥3 d、7 d、28 d和90 d抗压、抗折强度的影响。结果表明:单掺适量硫酸亚铁时,超硫酸盐水泥各龄期的抗压、抗折强度均有所提高,但掺量过大(>0.5%)时对早期(3 d)抗压、抗折强度不利;单掺硝酸钙时,超硫酸盐水泥各龄期的抗压、抗折强度均有所降低;复掺硫酸亚铁和硝酸钙时,超硫酸盐水泥各龄期的抗压、抗折强度较未掺和单掺时均有明显提高,其中,复掺1.5%硫酸亚铁和2.0%硝酸钙对强度的提高效果最好。
The supersulfate cement was prepared with slag,and the effects of ferrous sulfate and calcium nitrate on the compressive and flexural strength of supersulfate cement at 3 d,7 d,28 d and 90 d were studied.The results show that the compressive and flexural strength of supersulfate cement at all ages are improved with the appropriate content of ferrous sulfate alone,but the early compressive and flexural strength(3 d)are not good when the content is too large(>0.5%).When adding calcium nitrate alone,the compressive and flexural strength of each age of supersulfate cement decrease.When mixed with ferrous sulfate and calcium nitrate,the compressive and flexural strength of supersulfate cement at each age are significantly improved compared with those of blank group and single adding group,among them,mixed with 1.5%ferrous sulfate and 2.0%calcium nitrate has the best effect.
作者
季军荣
武双磊
周威杰
奚莹莹
周润铎
周洲
JI Jun-rong;WU Shuang-lei;ZHOU Wei-jie;XI Ying-ying;ZHOU Run-duo;ZHOU Zhou(Chongzuo South Cement Co.,Ltd.,Chongzuo 532201,China;School of Materials Science and Engineering,Zhejiang University,Hangzhou 310027,China)
出处
《混凝土与水泥制品》
2023年第1期79-83,共5页
China Concrete and Cement Products
关键词
超硫酸盐水泥
硫酸亚铁
硝酸钙
抗压强度
抗折强度
Supersulfate cement
Ferrous sulfate
Calcium nitrate
Compressive strength
Flexural strength