摘要
A new 980 MPa advanced high-strength steel(AHSS) with excellent bendability and flangeability has been studied and industrially produced, typical of tensile strength, fractured elongation, and hole expansion ratio(HER) exceeding 980 MPa, 10%,and 30%,respectively.The 90° V-type bending perpendicular to the rolling direction can satisfy the R/t=1.0 requirement, indicating excellent bendability.Systematic evaluations of industrial trial-produced 980 MPa hot-rolled AHSS have been conducted, including microstructure, tensile properties in three directions, HER,bendability, fatigue limit strength, and forming limit.The microstructure of the newly developed 980 MPa AHSS primarily consists of fine bainite and a small amount of martensite-austenite constituent.The practical yield and tensile strength are higher than 800 and 980 MPa, respectively, with typical elongation of 13% and HER of around 40%.The good combination of the newly developed 980 MPa AHSS is primarily attributed to the fine bainitic microstructure, resulting in excellent flangeability and bendability.In addition, the newly developed 980 MPa AHSS has good fatigue and forming properties, making it suitable for the production of chassis and suspension components.