摘要
Ti-Al-V-Zr quaternary titanium alloys were designed followingα-{[Al-Ti12](AlTi2)}17-n+β-{[Al-Ti12Zr2](V3)}n,where n=1-7(the number ofβunits),on the basis of the dual-cluster formula of popular Ti-6Al-4V alloy.Such an alloying strategy aims at strengthening the alloy via Zr and V co-alloying in theβ-Ti unit,based on the originalβformula[Al-Ti14](V2Ti)of Ti-6Al-4V alloy.The microstructures of the as-cast alloys by copper-mold suction-casting change from pureα(n=1)toα+α’martensite(n=7).When n is 6,Ti-5.6Al-6.8V-8.1Zr alloy reaches the highest ultimate tensile strength of 1,293 MPa and yield strength of 1,097 MPa,at the expense of a low elongation of 2%,mainly due to the presence of a large amount of acicularα’martensite.Its specific strength far exceeds that of Ti-6Al-4V alloy by 35%.