High piezo/photocatalytic efficiency of Ag/Bi_(5)O_(7)I nanocomposite using mechanical and solar energy for N2 fixation and methyl orange degradation

In this work,Ag/Bi_(5)O_(7)I nanocomposite was prepared and firstly applied in piezo/photocatalytic reduction of N2 to NH3 and methyl orange(MO)degradation.Bi_(5)O_(7)I was synthesized via a hydrothermal-calcination method and shows nanorods morphology.Ag nanoparticles(NPs)were photo deposited on the Bi_(5)O_(7)I nanorods as electron trappers to improve the spatial separation of charge carriers,which was confirmed via XPS,TEM,and electronic chemical analyses.The catalytic test indicates that Bi_(5)O_(7)I presents the piezoelectric-like behavior,while the loading of Ag NPs can strengthen the character.Under ultrasonic vibration,the optimal Ag/Bi_(5)O_(7)I presents high efficiency in MO degradation.The degradation rate is determined to be 0.033 min
1,which is 4.7 folds faster than that of Bi_(5)O_(7)I.The Ag/Bi_(5)O_(7)I also presents a high performance in piezocatalytic N2 fixation.The piezocatalytic NH3 generation rate reaches 65.4 μmol L^(-1)g^(-1)h^(-1)with water as a hole scavenger.The addition of methanol can hasten the piezoelectric catalytic reaction.Interestingly,when ultrasonic vibration and light irradiation simultaneously act on the Ag/Bi_(5)O_(7)I catalyst,higher performance in NH3 generation and MO degradation is observed.However,due to the weak adhesion of Ag NPs,some Ag NPs would fall off from the Bi_(5)O_(7)I surface under long-term ultrasonic vibration,which would greatly reduce the piezoelectric catalytic performance.This result indicates that a strong binding force is required when preparing the piezoelectric composite catalyst.The current work provides new insights for the development of highly efficient catalysts that can use multiple energies.