摘要
The influence of sodium dodecyl sulfate(SDS)on morphology and chemical composition of corrosion product layer formed onα-Mg matrix and cathodic Al-Mn intermetallic was systematically investigated by using FIB and TEM analysis for the first time to disclose the underlying inhibition mechanism.A porous corrosion bi-layer composed of crystalline MgO and Mg(OH)_(2)was observed on both ofα-Mg and Al-Mn intermetallic.It was found that a passive inner layer was deposited onα-Mg after immersion in SDS-containing NaCl solution,which can be ascribed to steady-state growth of magnesium and aluminum oxide under the protection of hydrophobic group of SDS.The inhibition mechanism of the inhibitor was mainly associated with formation of dense oxide layer onα-Mg matrix and preferential adsorption of SDS on the corrosion layer deposited on Al-Mn intermetallic.
基金
financial support from National Natural Science Foundation of China(No.52071067)
the Fundamental Research Funds for the Central Universities(N2002009)。