摘要
稀土掺杂石英光纤具有物化性能稳定、机械强度高、易于系统集成等优点,是目前光纤激光器最核心的增益介质,但其稀土掺杂浓度一般较低(<2%)。利用溶胶凝胶法和高温烧结工艺制备了Tm^(3+)掺杂浓度为8.29×10^(20) cm^(-3)的高硅氧玻璃,并表征了其光谱性能。采用溶胶镀膜和二次熔融拉锥方法制备了芯径约为4μm、外径为125μm的石英光纤,其可与商用无源光纤进行熔接。利用全光纤化线性腔结构,以制备的不同长度掺Tm^(3+)石英光纤作为增益介质,均可实现1947 nm激光输出,光信噪比约为70 dB;当光纤长度为4.6 cm时,斜率效率高达14.1%;同时搭建了掺铥光纤放大器,测得光纤小信号净增益系数为0.48 dB/cm。研究结果表明,该新型光纤制备方法可为高浓度掺铥石英光纤提供新途径,有望推动其在2.0μm单频及高重频锁模光纤激光器中的应用。
Objective The 2.0μm-band single-frequency laser has the advantages of narrow linewidth,low noise,and good monochromaticity,which is widely used in many fields,such as precision measurement,spaceborne lidar,and highresolution spectroscopy.Compared with multi-component glass fibers,the rare-earth-doped silica fiber is the core gain medium of fiber lasers,which boasts stable physical and chemical properties,high mechanical strength,and easy system integration.However,it is difficult to achieve the high-concentration doping of rare earth ions by traditional fabrication processes.There is still a gap in the doping concentration between the reported multi-component glass and the silica glass prepared by mature modified chemical vapor deposition(MCVD)combined with the liquid-phase doping process.Used in the short gain fiber for single-frequency lasers based on a distributed Bragg reflection(DBR)structure,the highly Tm^(3+)-doped technique ensures that the fiber has higher effective absorption to the pump source and a lower laser output threshold,which is more conducive to improving the laser performance of the system.For the high gain medium of 2.0μm-band single-frequency lasers,how to further improve the concentration of Tm^(3+)in silica glass becomes the focus of this paper.Methods We use Tetracthoxysilane(TEOS)as the silicon source,Al2O3 as the network-forming body,and La2O3 as the dispersant of silica glass to prepare highly Tm^(3+)-doped silica sol.Firstly,the high silica glass with the Tm^(3+)doping concentration of 8.29×10^(20) cm^(−3) is prepared by the sol-gel method and high-temperature sintering technology,which has good optical quality,and its spectral properties are characterized.Secondly,the sol-gel coating and melting taper drawing methods are combined innovatively to coat the inner wall of the silica capillary tube.After the film is heat-treated and tapered step by step,the silica fiber with a core diameter of about 4μm and a cladding diameter of 125μm is prepared,and the doping concentration of Tm^(3+)can reach as high as 8.29×10^(20) cm^(−3) in the silica fiber.This highly Tm^(3+)-doped silica fiber could be easily fusion-spliced with commercial passive silica fibers.Finally,an all-optical fiber laser system with a DBR structure is built to test the laser performance.Results and Discussions The physical properties of the highly Tm^(3+)-doped silica fiber are measured,which shows the element distribution and the refractive index distribution at the end face of the optical fiber(Fig.4).The all-fiber short cavity laser system(Fig.6)is independently built.The 808 nm laser is used to pump the highly Tm^(3+)-doped silica fibers with different lengths of 2.3 cm,4.6 cm,and 6.5 cm,and the highest slope efficiency of 14.1%is obtained when the fiber length is 4.6 cm.When the pump power is 250 mW,the optical signal-to-noise ratio(SNR)can be about 70 dB(Fig.7).The silica fiber with a length of 2.3 cm is selected to test the gain performance of the Tm^(3+)-doped silica fiber.When the seed source power is−9.34 dBm,the net small-signal gain coefficient is 0.48 dB/cm(Fig.9).Meanwhile,the loss coefficient is 1.22 dB/cm at 1310 nm,and the absorption coefficient of Tm^(3+)-doped silica fibers at 808 nm is 2.56 dB/cm.The data indicate that the input signal can be effectively amplified.Conclusions In this paper,we fabricate highly Tm^(3+)-doped high silica glass with a concentration of 8.29×10^(20) cm^(−3) by the sol-gel method and high-temperature sintering process.The highly Tm^(3+)-doped silica fiber with a core diameter of about 4μm and a cladding diameter of 125μm is also prepared by the sol-gel coating and double melting taper drawing methods.For better laser performance of the highly Tm^(3+)-doped high silica fiber prepared by this innovative process,the follow-up work will be carried out from the following two aspects:the composition control of the core glass and the optimization of the coating process.In terms of composition,the glass with the best fluorescence can be selected through different components.In terms of coating technology,the film thickness can be designed and adjusted,and the core size is adjusted to achieve better NA and mode-field matching when the silica fiber is fused with passive optical fibers.Meanwhile,a 789 nm source can be selected to further study the performance of fiber lasers.To sum up,this fiber preparation method has the potential to realize highly Tm^(3+)-doped silica fibers,which is expected to be applied in 2.0μm single-frequency fiber lasers and passively mode-locked fiber lasers with a high fundamental repetition rate.
作者
沈骁
杨广利
王亚飞
陈应刚
于春雷
韦玮
胡丽丽
Shen Xiao;Yang Guangli;Wang Yafei;Chen Yinggang;Yu Chunlei;Wei Wei;Hu Lili(College of Electronic and Optical Engineering&College of Flexible Electronics(Future Technology),Nanjing University of Posts and Telecommunications,Nanjing 210023,Jiangsu,China;Laboratory of High Power Laser Components,Shanghai Institute of Optics and Fine Mechanics,Chinese Academy of Sciences,Shanghai 201800,China;School of Physics and Optoelectronic Engineering,Hangzhou Institute for Advanced Study,UCAS,Hangzhou 310024,Zhejiang,China)
出处
《光学学报》
EI
CAS
CSCD
北大核心
2023年第4期104-111,共8页
Acta Optica Sinica
基金
国家自然科学基金面上项目(62075099,62074082)
企业横向课题(2021外305,2021外398)。