摘要
A type of heat-curing phosphate binder was proposed,and orthogonal experiments based on the tensile strength of sand samples determined that the optimal composition of the binder was phosphoric acid:water:aluminum hydroxide:magnesium oxide:boric acid=300:70:60:9:8.Adding 10%polyvinyl alcohol(PVA)solution during the sand mixture process can significantly improve the 24 h tensile strength of sand samples.When adding 30 g phosphate binder and 8 g 10%PVA solution,the initial tensile strength of the sample is 0.76 MPa,the room temperature tensile strength is 2.29 MPa,and the 24 h tensile strength is 1.73 MPa.The heat-curing modified phosphate sand mold has high tensile strength and low gas generation,which can meet general casting production requirements.