Li(_(1+x))2MgTi3O8(0.0≤x≤0.10)ceramics with Li non-stoichiometric ratios were prepared by the solidstate reaction method to inhibit the volatilization of Li.The effects of the Li non-stoichiometric ratios on the sintering behavior,crystal structure,microscopic morphology,Raman vibrations,electron density,and dielectric properties of Li(_(1+x))2MgTi3O8 ceramics were systematically investigated.The Li(1+0.06)_(2)MgTi_(3)O_(8)ceramics demonstrate the best dielectric properties withεr=26.33,Q×f=69435 GHz(@6.87 GHz,54%improvement),tf=2.95×10^(-6)℃^(-1).For the non-intrinsic factors,the high relative density(97.15%)and larger grain size(16.78 mm)allow the dielectric properties to be improved.As for the intrinsic factors,a reasonable excess of Li improves the bond ionicity of the MgdO bond,the lattice energy of the TidO bond,and the electron cloud density,thus optimizing the dielectric properties.Raman spectroscopy leads to the same result from the point of view of lattice vibrations.At the same time,the distortion of the polyhedra is also improved,so that tf also approaches 0.The improved Li(1+0.06)2MgTi3O8 has potential applications in microwave communication technology.
基金
supported by the National Natural Science Foundation of China(Grant No.51902042)
the National Key Scientific Instrument and Equipment Development Project(No.51827802)
the Major Science and Technology Specific Projects of Sichuan Province(No.2019ZDZX0026).