TiO_(2) nanoparticles(NPs)in the size of-25 nm,namely P25,are very common material as the electron collecting layer in dye-sensitized solar cells(DSsCs).However,the light-scattering improvement of TiO2 NP photoelectrodes is stll a challenge.Here,we built TiO2 cavities on the top of the TiO2 NP layer by using carbonaceous microspheres as the template,forming the TiO_(2) cavity/nanoparticle(C/NP)photoelectrode for the application in DSSCs.The cavity amount in the TiO_(2) C/NP photoelectrode was controlled by adjusting the weight ratio of carbonaceous microspheres.SEM results confirm the successful formation of the double-layered TiO_(2) C/NP electrode.J-V tests show that the optimized TiO_(2) C/NP electrode prepared with 25 wt.%carbonaceous microspheres contributes to remarkable improvement of the short-circuit current density(Jsc)and the power conversion efficiency(PcE).The best photovoltaic performance solar cell with the PCE of 9.08%is achieved with the optimized TiO_(2) C/NP photoelectrode,which is over 98% higher than that of the TiO_(2) NP photoelectrode.Further investigations of UV-vis DRS,IPCE,OCVD,and EIS demonstrate that the competition between light scattering effect and charges recombination in this TiO_(2) C/NP photoelectrode is responsiblefor the PCE enhancement.
基金
This work was financially supported by the National Natural Science Foundation of China(Grant No.51862007)
the Western Youth Scholars Program of Chinese Academy of Sciences,and the Young Doctor Fund Project of Gansu Provincial Department of Education(Grant No.2022QB-156).