Construction of hydrangea-like core-shell SiO_(2)@Ti_(3)C_(2)T_(x)@CoNi microspheres for tunable electromagnetic wave absorbers

Ti_(3)C_(2)T_(x)MXene shows great potential in the application as microwave absorbers due to its high attenuation ability.However,excessively high permittivity and self-stacking are the main obstacles that constrain its wide range of applications.To tackle these problems,herein,the microspheres of SiO_(2)@Ti_(3)C_(2)T_(x)@CoNi with the hydrangea-like core-shell structure were designed and prepared by a combinatorial electrostatic assembly and hydrothermal reaction method.These microspheres are constructed by an outside layer of CoNi nanosheets and intermediate Ti_(3)C_(2)T_(x)MXene nanosheets wrapping on the core of modified SiO_(2),engendering both homogenous and heterogeneous interfaces.Such trilayer SiO_(2)@Ti_(3)C_(2)T_(x)@CoNi microspheres are“magnetic microsize supercapacitors”that can not only induce dielectric loss and magnetic loss but also provide multilayer interfaces to enhance the interfacial polarization.The optimized impedance matching and core-shell structure could boost the reflection loss(RL)by electromagnetic synergy.The synthesized SiO_(2)@Ti_(3)C_(2)T_(x)@CoNi microspheres demonstrate outstanding microwave absorption(MA)performance benefited from these advantages.The obtained RL value was-63.95 dB at an ultra-thin thickness of 1.2 mm,corresponding to an effective absorption bandwidth(EAB)of 4.56 GHz.This work demonstrates that the trilayer core-shell structure designing strategy is highly efficient for tuning the MA performance of MXene-based microspheres.