摘要
研究了硫化温度和硫化时间对天然橡胶(NR)和NR/反式丁戊橡胶(TBIR)并用胶应用性能的影响。结果表明,在相同的硫化温度下,NR与NR/TBIR并用胶的焦烧时间、工艺正硫化时间和交联密度几乎一致。对比140℃、150℃和160℃硫化温度下NR和NR/TBIR硫化胶的性能,NR/TBIR并用胶在160℃下硫化时磨耗性能和滚动阻力优势最大,150℃硫化时疲劳性能优势最大。对比160℃下的硫化时间,发现其变化不会明显影响TBIR在NR体系中的磨耗性能、滚动阻力和疲劳性能优势的发挥。
The effects of vulcanization temperature and time on the application properties of NR and NR/TBIR blends were studied.The results showed that,the scorch time,optimum curing time and crosslinking density of NR and NR/TBIR blends were almost the same at the same curing temperature.The properties of NR and NR/TBIR vulcanizated at 140℃,150℃and 160℃were investigated.Compared with NR vulcanizates,NR/TBIR vulcanized at 160℃showed the greatest advantages in wear resistance and rolling resistance.And the fatigue resistance of NR/TBIR vulcanized at 150℃was best.It was also found that the change of vulcanization time did not significantly affect the advantages of NR/TBIR vulcanizates in the wear resistance,rolling resistance and fatigue resistance compared with NR vulcanizates.
作者
王浩
李兰阁
赵涛
葛怀涛
王日国
翟红莲
栾波
WANG Hao;LI Lange;ZHAO Tao;GE Huaitao;WANG Riguo;ZHAI Honglian;LUAN Bo(Shandong Chambroad Holding Co.,Ltd.,Binzhou 256500,China;Shandong Huaju Polymer Materials Co.,Ltd.,Binzhou 256500,China;Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization,Binzhou 256500,China)
出处
《弹性体》
CAS
北大核心
2023年第1期54-57,共4页
China Elastomerics
基金
国家重点研发计划项目(SQ2022YFB3700063)
山东省重大科技创新工程项目(2021CXGC010901)。
关键词
并用胶
反式丁戊橡胶
硫化条件
动态疲劳性能
滚动阻力
磨耗性能
blends
trans-1,4-poly(butadiene-co-isoprene)rubber(TBIR)
vulcanization condition
dynamic fatigue property
rolling resistance
wear resistance