摘要
The Al-5Cu alloys were prepared by different treatment methods,including adding a refiner Al-5Ti-1B,exerting a rotating magnetic field(RMF),and compound treatment of both refiner and RMF.The effects of treatment methods on the microstructure,properties,and solid solubility of the Al-5Cu alloy were investigated.The optimal magnetic field parameters and addition amount of refiner were confirmed by experiment.Results show that either RMF or adding refiner Al-5Ti-1B alone can refine the grain size,and the refining effect can be further improved by a compound refining treatment with optimized magnetic field parameters(120 A current and 8 Hz frequency) and 1.0wt.% Al-5Ti-1B refiner(RMF*+Al-5Ti-1B*).The average grain size is decreased to 68.1 μm,which is 60.8%,21.1%,and 83.5% lower than that of the alloy treated by the optimized rotating magnetic field,the Al-5Ti-1B refiner,and the alloy without any treatment,respectively.The tensile strength and elongation of the alloy reach 232.5 MPa and 18.6%,respectively,which are obviously higher than those of the alloys treated by rotating magnetic field,Al-5Ti-1B refiner,and the alloy without any treatment,respectively.Additionally,the solid solubility of the alloy is also obviously improved compared to the alloys treated by other methods.