This work investigated the aging effects on the rheological properties of high viscosity modified asphalt(HVMA).First,the high-and low-temperature rheological properties were measured by a dynamic shear rheometer and a bending beam rheometer,respectively.The aging mechanism was then tested using an Fourier transform infrared spectroscopy and a scanning electron microscope.Besides,a study was performed to compare the aging effects on the rheological properties of HVMA,crumb rubber modified asphalt(CRMA),and neat asphalt(SK-90).The experimental results showed that the effects of the long-term aging on HVMA exceeded those of short-term aging.The complex shear modulus of the HVMA was improved by the aging in the whole frequency range.The complex shear modulus of the HVMA after the long-term aging was larger than after the short-term aging.Thus,the aging improved the high-temperature viscoelastic performance of HVMA.With a decrease in temperature from-12℃to-24℃,the low-temperature viscoelastic performance of HVMA decreased since its stiffness modulus and low continuous grading temperature increase.Both of the short-and long-term aging of HVMA were caused by an oxidation reaction,while modifier swelling also happened after long-term aging.Compared to CRMA and SK-90,aging had a limited influence on the high-and low-temperature rheological properties of HVMA.
基金
supported by the National Key R&D Program of China(Grant No.2018YFB1600200)
the Fok YingTong Education Foundation(Grant No.161072)
the Youth Top-notch Talent Support Program of Shaanxi Province
the Fundamental Research Funds for the Central Universities(Grant No.300102219317)。