Ultrafine SnO_(2)in situ modified graphite felt derived from metal-organic framework as a superior electrode for vanadium redox flow battery

Metal-organic framework(MOF)and its derivatives have low-cost,controllable structure,and good catalytic performance,which are often used in the electrochemical field.In this work,SnO_(2)in situ modified graphite felt(SnO_(2)/GF)is prepared by hydrothermal method then simple thermal treatment using Sn-based MOF(Sn-MOF)as precursor.SnO_(2)is uniformly and firmly distributed on the GF surface rather than the common agglomeration and poor bonding of metal oxides on carbon-based electrodes,providing stable active centers for the VO^(2+)/VO_(2)^(+)and V^(2+)/V^(3+)redox reactions.At250 mA·cm^(-2),the energy efficiency of the battery with SnO_(2)/GF remains at 63.2%,while the blank one has failed.The former battery,at 100 mA·cm^(-2),has higher energy efficiency and good cycle stability(over 200 cycles).The battery performance of this study is better than that of most previous report in metal oxide-related work.This work obtains high-performance composite electrode by simple treatment of MOF,which provides a reference for the application of MOF in vanadium redox flow battery.