摘要
Selective laser melting(SLM)technology based on atomized powder was used to fabricate Al-8.5Fe-1.3V-1.7Si(wt%)alloy parts.The microstructure and crack characterization of SLM samples fabricated at various conditions were presented.Results show that the cracks appear periodically along the building direction,initiate preferably at the outer edges of the as-built samples and propagated along the remelting border zone(RBZ)into deposited layers.Solid-phase cracking is proposed according to the fracture morphology.The thermal-induced residual stress during SLM combined with the precipitation of relatively large-sized Al_mFe phase in the RBZ results in the formation of cracks.Enhancing scanning speed and hatch distance enable to reduce the cracking sensitivity.The crack-free Al-8.5Fe-1.3V-1.7Si parts can be fabricated at optimized parameters of laser power of 320 W,scanning speed of 1000 mm·s^(-1)and hatch distance of0.10 mm along with proper laser pre-heating procedure.The samples built horizontally show good ultimate tensile properties of 454 MPa in average with the elongation of7.2%.
出处
《Rare Metals》
SCIE
EI
CAS
CSCD
2023年第4期1353-1362,共10页
稀有金属(英文版)
基金
financially supported by the National High-Tech Program of China(No.21100002013101006)。