介绍了外援型自修复涂层的修复机理,针对涂层缺陷修复不理想的问题,提出优化措施。总结了本征型自修复涂层的修复机理、存在的问题及优化措施。分析了智能防腐涂层在国内核电领域的应用前景和需要开展的应用研究。对智能防腐涂层未来的发展方向进行了展望。
The repair mechanism of the self-repairing coating with foreign aid is introduced,and the optimization measures are proposed to solve the problem that the repair of coating defects is not ideal.The repair mechanism,existing problems and optimization measures of the intrinsic self-repairing coating are summarized.The application prospect and necessary application research of smart anti-corrosion coating in domestic nuclear power are analyzed.The future development direction of smart anti-corrosion coating is prospected.
作者
许超
肖调兵
乔泽
陈银强
章强
张飞
XU Chao;XIAO Tiaobing;QIAO Ze;CHEN Yinqiang;ZHANG Qiang;ZHANG Fei(China Nuclear Power Operation Technology Corporation Co.,Ltd.,Wuhan 430223,China;Fujian Fuqing Nuclear Power Co.,Ltd.,Fuqing 350318,China)
出处
《腐蚀与防护》
CAS
CSCD
北大核心
2023年第4期65-71,81,共8页
Corrosion & Protection
关键词
外援型自修复涂层
本征型自修复涂层
核电站
external self-repairing coating
intrinsic self-healing coating
nuclear power plant