摘要
Imposing phase engineering to porous materials is promising to realize outperforming electrocatalytic performances by taking advantages of the merits of porous nanoarchitecture and heterophase structure.In this work,amorphous/crystalline ruthenium oxide(RuO_(2))porous particles with rationally regulated heterophases are successfully prepared by integrating the phase engineering into the porous material synthesis.The resultant defect-rich amorphous/crystalline RuO_(2)porous particles exhibit excellent electrocatalytic performance toward the oxygen evolution reaction,achieving a low overpotential of 165 mV at a current density of 10 mA·cm^(−2)and a high mass activity up to 133.8 mA·cm^(-2)at a low overpotential of 200 mV.This work indicates that the synergistic effect of amorphous/crystalline heterophase and porous structural characteristics enables RuO_(2)to trigger a superior electrocatalytic activity.