Effect of annealing on properties of Al/steel composite plates prepared by surface oxidation treatment before cold roll bonding

Al/steel composite plate has a wide application prospect,but great differences in properties between Al and steel are observed.It is difficult to obtain high bonding strength by the traditional cold roll bonding process.Al/steel composite plate was thus prepared by cold roll bonding at a reduction rate of 60%after oxidation treatment on the surface to be composited on the steel side.The heat treatment of holding at 400℃ for 1 h and cooling with the furnace was then adopted.The bonding strength,microstructure,and properties of the Al/steel composite plate before and after annealing were analysed and compared through shear test,bending test,tensile test,and micro-characterization.Results show that the shear strengths of the interface before and after annealing are 100 and 80 MPa,respectively.Although the shear strength of the annealed Al/steel composite plate decreases,the bending and overall tensile properties of the composite plate are improved,showing better mechanical properties.