Efficient Semi‑Transparent Wide‑Bandgap Perovskite Solar Cells Enabled by Pure‑Chloride 2D‑Perovskite Passivation

Wide-bandgap(WBG)perovskite solar cells suffer from severe non-radiative recombination and exhibit relatively large opencircuit voltage(V_(OC))deficits,limiting their photovoltaic performance.Here,we address these issues by in-situ forming a well-defined 2D perovskite(PMA)_(2)PbCl_(4)(phenmethylammonium is referred to as PMA)passivation layer on top of the WBG active layer.The 2D layer with highly pure dimensionality and halide components is realized by intentionally tailoring the side-chain substituent at the aryl ring of the post-treatment reagent.First-principle calculation and single-crystal X-ray diffraction results reveal that weak intermolecular interactions between bulky PMA cations and relatively low cation-halide hydrogen bonding strength are crucial in forming the well-defined 2D phase.The(PMA)_(2)PbCl_(4)forms improved type-I energy level alignment with the WBG perovskite,reducing the electron recombination at the perovskite/hole-transport-layer interface.Applying this strategy in fabricating semi-transparent WBG perovskite solar cells(indium tin oxide as the back electrode),the V_(OC)deficits can be reduced to 0.49 V,comparable with the reported state-of-the-art WBG perovskite solar cells using metal electrodes.Consequently,we obtain hysteresis-free 18.60%-efficient WBG perovskite solar cells with a high V_(OC)of 1.23 V.