摘要
The blend was synthesised with bismaleimide(BMI)resin and bisphenol A-based cyanate ester(BADCy)resin.The BMI/BADCy copolymer showed excellent dielectric and thermal conductivity properties.The volume resistivity of the copolymer was a little lower than BADCy system.The volume resistivity of blend was 7.8×10^(15)Ω·cm when the BMI content was 20 wt%,which still showed good insulation performance.The dielectric property of modified BADCy copolymer remained the good stability from 0.1 Hz to 1 MHz.Compared to pure BADCy system,the breakdown property of BMI/BADCy blend reached the maximum value of 77.9 kV/mm when the content of BMI was 20 wt%,which was still about 1.22 times.The thermal property and thermal conductivity property of the copolymer were higher than BADCy system.
基金
This work was financially supported by the NSFC(no.51407134)
China Postdoctoral Science Foundation(nos.2016M590619,2016M601878)
Natural Science Foundation of Shandong Province(no.ZR2016EEQ28)
Special Scientific Research Program of Shaanxi Provincial Department of Education(no.16JK1043)。