摘要
Cellulose microspheres were fabricated on the basis of sol-gel transition using NaOH/urea/H_(2)O as the solvent system.These microspheres had an average diameter of about 30μm.Upon modification with Fe_(3)O_(4) and poly(DOPAm-co-PFOEA),superhydrophobic magnetic cellulose microspheres were generated,which were analyzed by FTIR,TG,XRD,XPS and water contact angle tests.Magnetic cellulose microspheres contained approximately 15 wt%of Fe_(3)O_(4).Poly(DOPAm-co-PFOEA)/Fe_(3)O_(4)/cellulose microspheres and had a low surface energy and a high water-repellency.These superhydrophobic microspheres were also converted into liquid marbles via an easily scalable process.