摘要
针对硬脆材料的硬度高,传统的碳化硅磁性磨料研磨效率低、磨料寿命短等问题,开发以金刚石颗粒作为研磨相的磁性磨料。以高纯铁粉为铁基相,金刚石为研磨相,采用树脂黏结法制备金刚石磁性磨料。以K9玻璃为加工对象,比较金刚石磁性磨料和碳化硅磁性磨料磁力研磨K9玻璃时的使用寿命和加工效率。实验得到金刚石磁性磨料的寿命为60.00 min,能够将K9玻璃的平均表面粗糙度R_(a)加工至0.036μm,在使用寿命内能够加工的工件为4.6件;而碳化硅磁性磨料的寿命仅有40.00 min,只能将K9玻璃的平均表面粗糙度R_(a)加工至0.222μm,在使用寿命内能够加工的工件为3.6件。金刚石颗粒作为研磨相能够有效地提高磁性磨料的使用寿命、加工能力以及磁力研磨的加工效率。
The hardness of hard-brittle materials is high,which results in the low lapping efficiency of traditional silic-on carbide magnetic abrasive and short abrasive life.In view of this situation,a magnetic abrasive with diamond particle as lapping grit was developed.Using high purity iron powder as iron-based phase and diamond particle as abrasive,dia-mond magnetic abrasives were prepared by resin bonding method.K9 glass was chosen as the part being machined.The service life and processing efficiency of magnetic lapping K9 glass were compared between with diamond magnetic ab-rasives and with silicon carbide magnetic abrasives.The lifespan of diamond magnetic abrasive is 60.00 min,and the number of work-piece which can be machined is 4.6 pieces in the service life.The average surface roughness of K9 glass reaches 0.036μm.However,the service life of the silicon carbide magnetic abrasive particles is only 40 min,and the average surface roughness of the K9 glass workpiece can only be processed to 0.222μm.Besides,the number of workpieces that can be processed during the service life is 3.6 pieces.Diamond magnetic abrasives can effectively im-prove the service life,the processing capacity of magnetic abrasives,and the processing efficiency of magnetic grinding.
作者
董彦辉
牛风丽
任泽
盛鑫
朱永伟
DONG Yanhui;NIU Fengli;REN Ze;SHENG Xin;ZHU Yongwei(Nanjing University of Aeronautics and Astronautics,College of Mechanical&Electrical Engineering,Nanjing 210016,China)
出处
《金刚石与磨料磨具工程》
CAS
北大核心
2023年第3期379-385,共7页
Diamond & Abrasives Engineering
基金
国家自然科学基金联合基金(U20A20293)。
关键词
磁性磨粒
金刚石
碳化硅
使用寿命
加工效率
magnetic abrasive
diamond
silicon carbide
service life
lapping efficiency