摘要
Iron-pillared bentonite(FB)was prepared by Fe(III)modified bentonite,and then the composites(FB-OS)were prepared by iron-pillared bentonite and oyster shell powder.The composites were characterized by FTIR,SEM,TGA,and EDS,and the phosphorus removal test was carried out.The results showed that FB-OS contained a large amount of CaO.Its structure was compact,but there were gaps in it.The maximum bending stress and compressive strength were 43.7 N and 0.927 MPa,respectively.The phosphorus removal test showed that the phosphorus removal rate of FB-OS was more than 90%,and measured the maximum adsorption capacity was 48.31 mg/g.A large amount of spherical products were produced on the surface and inside of FB-OS after phos-phorus removal,it was speculated that spherical products were amorphous calcium phosphate in the paper.Ana-lysis indicated that there was chemical adsorption during phosphorus removal.The kinetic equation of phosphorus adsorption by FB-OS was qt=10:193t/1+2:574t (R^(2)=0.995).The adsorption rate was mainly controlled by outerfilm diffusion and intraparticle diffusion.
基金
supported by the Project of Guangdong Academy of Building Research Group Co.,Ltd.,China(No.0100RDY2022D0000036).