Low-temperature and flexible strategy to in-situ fabricate ZrSiO_(4)-based ceramic composites via doping and tuning solid-state reaction

Synthetic zircon(ZrSiO_(4))ceramics are typically fabricated at elevated temperatures(over 1500℃),which would lead to high manufacturing cost.Meanwhile,reports about preparing ZrSiO_(4)-based ceramic composites via controlling the solid-state reaction between zirconia(ZrO_(2))and silica(SiO_(2))are limited.In this work,we proposed a low-temperature strategy to flexibly design and fabricate ZrSiO_(4)-based ceramic composites via doping and tuning the solid-state reaction.Two ceramic composites and ZrSiO_(4) ceramics were in-situ prepared by reactive fast hot pressing(FHP)at approximately 1250℃ based on the proposed strategy,i.e.,a ZrSiO_(4)-SiO_(2) dual-phase composite with bicontinuous interpenetrating and hierarchical microstructures,a ZrSiO_(4)-ZrO_(2) dual-phase composite with a microstructure of ZrO_(2) submicron-and nano-particles embedded in a micron ZrSiO_(4) matrix,and ZrSiO_(4) ceramics with a small amount of residual ZrO_(2) nanoparticles.The results showed that the phase compositions,microstructure configurations,mechanical properties,and wear resistance of the materials can be flexibly regulated by the proposed strategy.Hence,ZrSiO_(4)-based ceramic composites with different properties can be easily fabricated based on different application scenarios.These findings would offer useful guidance for researchers to flexibly fabricate ZrSiO_(4)-based ceramic composites at low temperatures and tailor their microstructures and properties through doping and tuning the solid-state reaction.