摘要
A typical G-phase strengthened ferritic model alloy(1Ti:Fe-20Cr-3Ni-1Ti-3Si,wt.%)has been carefully studied using both advanced experimental(EBSD,TEM and APT)and theoretical(DFT)techniques.During the classic“solid solution and aging”process,the superfine(Fe,Ni)_(2)TiSi-L2_(1)particles densely precipitate within the ferritic grain and subsequently transform into the(Ni,Fe)_(16)Ti_(6)Si_(7)-G phase.In the meanwhile,the elemental segregation at grain boundaries and the resulting precipitation of a large amount of the(Ni,Fe)_(16)Ti_(6)Si_(7)-G phase are also observed.These nanoscale microstructural evolutions result in a remarkable increase in hardness(100-300 HV)and severe embrittlement.When the“cold rolling and aging”process is used,the brittle fracture is effectively suppressed without loss of nano-precipitation strengthening ef-fect.Superhigh yield strength of 1700 MPa with 4%elongation at break is achieved.This key improvement in mechanical properties is mainly attributed to the pre-cold rolling process which effectively avoids the dense precipitation of the G-phase at the grain boundary.These findings could shed light on the further exploration of the precipitation site via optimal processing strategies.
基金
This work was financially funded by the National Natural Science Foundation of China(Nos.51971082 and 52001098)
the National Post-doctoral Program for Innovative Talents(No.BX20200103)
the China Post-doctoral Science Foundation(No.2020M681092).The authors would like to thank Dr.Ivan Povstugar at ZEA-。