摘要
Ion irradiation is usually used to simulate neutron irradiation to accelerate the evaluation of the irradia-tion behavior of reactor materials.However,the validity of using a high damage rate of ion irradiation to simulate a low damage rate of neutron irradiation has always been a controversial topic.Here,the effect of two dose rates(2.94×10^(-6) and 7.35×10^(-5) dpa s^(-1))on the characteristics and evolution of dislo-cation loops in palladium was studied in situ during 30 keV H2+irradiation using transmission electron microscopy.The dose rate obviously affected the nucleation rate and growth rate of dislocation loops,the types(Frank loops or perfect loops)of dislocation loops,and the irradiation hardening and total damage obtained from the product of average loop size and loop density.At the same irradiation dose,a high dose rate would lead to high loop density,small average loop size,low loop growth rate,and low irra-diation hardening and damage induced by loops in pure Pd.Meanwhile,it was found for the first time that a high dose rate was beneficial to the generation of perfect dislocation loops.The effect of dose rate was attributed to the different dynamic equilibrium results between the effective generation rate of point defects and their absorption rate by existing sinks.The present results show that the effect of dose rate should be considered when using ion irradiation to simulate neutron irradiation to evaluate the irradiation damage to materials.
基金
supported by the National Science Fund for Distinguished Young Scholars of China (Grant No.12225506)
the National Natural Science Foundation of China (Grant No.U1967211 and 11975191)
the National MCF Energy R&D Program (Grant No.2022YFE03110000).