The effect of Ce content(0–1.6 wt.%)on the modification of Mg_(2)Si phase in the as-cast Mg-5Al-2Si alloy was investigated.The original Chinese script type Mg_(2)Si phase was refined distinctly and transformed to dispersive block shape gradually by adding Ce element.The length of Chinese script type Mg_(2)Si phase was reduced from 110 to 50μm with increasing Ce content to 1.6 wt.%.The results calculated by Pandat software indicated that the added Ce element first combined with Si to form CeSi_(2)phase,which could serve as the heterogeneous nucleation of Mg_(2)Si phase due to the small lattice mismatch of 7.97%.The modification of Mg_(2)Si phase was mainly attributed to the facts that Ce changed the growth steps of Mg_(2)Si phase and CeSi_(2)promoted the nucleation of Mg_(2)Si phase.With increasing Ce content from 0 wt.%to 1.6 wt.%,the YS,UTS and EL at 150℃were improved from 67.7 MPa,91.2 MPa and 1.6%to 84.2 MPa,128 MPa and 7.5%,respectively.
基金
supported by the Major Science and Technology projects in Qinghai province (2018-GX-A1)
Global Frontier Program through the Global Frontier Hybrid Interface Materials (GFHIM) of the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (Grant No. 2013M3A6B1078874)
funded by Shanghai Science and Technology Committee (Grant No. 18511109302)
the National Natural Science Foundation of China (Grant No. 51825101)