摘要
The organic carbon source coating LiFe_(x)Mn_(1-x)PO_(4)suffers from the problem of non-uniform carbon cladding.Too thick carbon cladding layer instead hinders the de-embedding of lithium ions.In this paper,we choose cornstalk as the carbon source,then LiFe_(0.5)Mn_(0.5)PO_(4)@cornstalk-C(LFMP@C-C)with 3D anchoring structure is prepared by the solvothermal method.The results show that the LFMP with cornstalk as the carbon source has better performance compared to the sucrose-coated LFMP material(LFMP@C).The discharge capacity of LFMP@C-C is 116 mAh/g for the first cycle at 1 C and the capacity retention rate is 94.0%after 500 cycles,and the discharge capacity of LFMP@C-C is more than 17.17%higher than that of LFMP@C.
基金
supported by CITIC Dameng Mining Industries Limited-Guangxi University Joint Research Institute of manganese resources utilization and advanced materials technology,Guangxi University-CITIC Dameng Mining Industries Limited Joint base of postgraduate cultivation,National Natural Science Foundation of China(No.11364003)
Guangxi Innovation Driven Development Project(Nos.AA17204100,AA18118052)
the Natural Science Foundation of Guangxi Province(No.2018GXNSFAA138186)。