摘要
Halide perovskites with excellent piezoelectric properties,but their poor stability hinders their largescale application.Herein,a sandwich-structured halide perovskite flexible sensor with good stability was developed according to a three-step procedure as follows:(ⅰ) in-situ growth of wool keratinCsPbBr_(3)(WK-CsPbBr_(3)) using wool keratin in interfacial passivation and coating,(ⅱ) electrospinning of a wool keratin-CsPbBr_(3)/polyacrylonitrile(WCP) nanofiber film,and(ⅲ) coating of the WCP nanofiber with polydimethylsiloxane(PDMS) to obtain a sensor(WCPP).The sensor could generate a piezoelectric voltage of 7.8 V at a pressure of 6 kPa in the stages of pressing and releasing,and the output characteristics did not decline even after 10,000 cycles.Compared to the 4-month stability of the perovskite sensor,WCPP sensor exhibited the output performance even after 16 months,which indicated that wool keratin as a multidentate improved the stability of the halide perovskite.Additionally,the sensor displayed a self-cleaning property and could also light up 14 commercial LEDs.The close-loop recycling of the lead halide perovskite was achieved by dissolving the WCP nanofiber film in DMF and then reelectrospinning.Therefore,the method proposed is a step forward for achieving the commercialization of WK-CsPbBr_(3) and providing new avenues for further utilization of wool waste.
基金
funded by the National Natural Science Foundation of China (22178210)
the Innovation Capability Support Program of Shaanxi (2021TD-16)
Key Project of Natural Science Basic Research Program of Shaanxi Province (2023JC-XJ-12)
the Shaanxi Provincial “Special Support Plan for High-level Talents”。