Multicomponent mixed metallic hierarchical ZnNi@Ni@PEDOT arrayed structures as advanced electrode for high-performance hybrid electrochemical cells

Engineering multicomponent nanomaterials as an electrode with rationalized ordered structures is a promising strategy for fulfilling the high-energy storage needs of supercapacitors(SCs).Even now,the fundamental barrier to utilizing hydroxides/hydroxyl carbonates is their poor electrochemical performance,resulting from the significantly poor electrical conductivity and sluggish charge storage kinetics.Hence,a multilayered structural approach is primarily and successfully used to construct electrodes as one of the efficient approaches.This method has made it possible to develop well-ordered nanostructured electrodes with good performance by taking advantage of tunable approach parameters.Herein,we report the design of multilayered heterostructure porous zinc-nickel nanosheets@nickel flakes hydroxyl carbonates and/or hydroxides integrated with conductive PEDOT fibrous network(i.e.,ZnNi@Ni@PEDOT) via facile synthesis methods.The combined hybrid electrode acquires the features of high electrical conductivity from one part and various valance states from another one to develop a well-organized nanosheet/flake/fibrous-like heterostructure with decent mechanical strength,creating robust synergistic results.Thus,the designed binder-free ZnNi@Ni@PEDOT electrode delivers a high areal capacity value of 1050.1 μA h cm^(-2) at 3 mA cm^(-2) with good cycling durability,significantly outperforming other individual electrodes.Moreover,its feasibility is also tested by constructing a hybrid electrochemical cell(HEC).The assembled HEC exhibits a high areal capacity value of 783.8 μA h cm^(-2) at5 mA cm^(-2).and even at a high current density of 100 mA cm^(-2)(484.6 μA h cm^(-2)),the device still retains a rate capability of 61,82%,Also,the HEC shows maximum energy and power densities of0.595 mW h cm^(-2) and 77.23 mW cm^(-2),respectively,along with good cycling stability.The obtained energy storage capabilities effectively power various electronic components.These results provide a viable and practical way to construct a positive electrode with innovative heterostructures for highperformance energy storage devices and profoundly influence the development of electrochemical SCs.