FeCoNiCrMo high entropy alloy nanosheets catalyzed magnesium hydride for solid-state hydrogen storage

The catalytic effect of FeCoNiCrMo high entropy alloy nanosheets on the hydrogen storage performance of magnesium hydride(MgH_(2))was investigated for the first time in this paper.Experimental results demonstrated that 9wt%FeCoNiCrMo doped MgH_(2)started to dehydrogenate at 200℃and discharged up to 5.89wt%hydrogen within 60 min at 325℃.The fully dehydrogenated composite could absorb3.23wt%hydrogen in 50 min at a temperature as low as 100℃.The calculated de/hydrogenation activation energy values decreased by44.21%/55.22%compared with MgH_(2),respectively.Moreover,the composite’s hydrogen capacity dropped only 0.28wt%after 20 cycles,demonstrating remarkable cycling stability.The microstructure analysis verified that the five elements,Fe,Co,Ni,Cr,and Mo,remained stable in the form of high entropy alloy during the cycling process,and synergistically serving as a catalytic union to boost the de/hydrogenation reactions of MgH_(2).Besides,the FeCoNiCrMo nanosheets had close contact with MgH_(2),providing numerous non-homogeneous activation sites and diffusion channels for the rapid transfer of hydrogen,thus obtaining a superior catalytic effect.