Layer stacked SiO_(x) microparticle with disconnected interstices enables stable interphase and particle integrity for lithium-ion batteries

Severe mechanical fractu re and unstable interphase,associated with the large volumetric expansion/contraction,significantly hinder the application of high-capacity SiO_(x)materials in lithium-ion batteries.Herein,we report the design and facile synthesis of a layer stacked SiO_(x)microparticle(LS-SiO_(x))material,which presents a stacking structure of SiO_(x)layers with abundant disconnected interstices.This LS-SiO_(x)microparticle can effectively accommodate the volume expansion,while ensuring negligible particle expansion.More importantly,the interstices within SiO_(x)microparticle are disconnected from each other,which efficiently prevent the electrolyte from infiltration into the interior,achieving stable electrode/-electrolyte interface.Accordingly,the LS-SiO_(x)material without any coating delivers ultrahigh average Coulombic efficiency,outstanding cycling stability,and full-cell applicability.Only 6 cycles can attain>99.92%Coulombic efficiency and the capacity retention at 0.05 A g^(-1)for 100 cycles exceeds99%.After 800 cycles at 1 A g^(-1),the thickness swelling of LS-SiO_(x)electrode is as low as 0.87%.Moreover,the full cell with pure LS-SiO_(x)anode exhibits capacity retention of 91.2%after 300 cycles at 0.2 C.This work provides a novel concept and effective approach to rationally design silicon-based and other electrode materials with huge volume variation for electrochemical energy storage applications.