In this study,an integrative bioinspired coating system for antifouling and corrosion resistance was investigated,in which self-healing nanocapsules(tung oil calcium alginate,TO@CA),doped polyaniline and nano-titanium dioxide nanocomposites(SPAn–TiO_(2))and a biostructure metal surface were combined.The antifouling property of the bioinspired coating resulted from the synergistic antifouling effect of nano-TiO_(2)and acid-doped polyaniline in SPAn–TiO_(2).The protonated nitrogen with a positive charge in SPAn–TiO_(2)and the intrinsic bactericidal property of nano-TiO_(2)could damage negatively charged single-celled chlorella,endowing the composite coating with good antifouling performance(less algae attached on the surfaces after a 90-day antifouling test and a conductivity test).The composite bioinspired coating had excellent corrosion resistance,which was due to the good synergistic anticorrosion barrier effect of SPAn–TiO_(2)with TO@CA nanocapsules and the repairing ability of microcracks of TO@CA nanocapsules during the corrosion process.The bioinspired coating with 2 wt%SPAn–TiO_(2)and 2 wt%TO@CA nanocapsules exhibited a better adhesion,corrosion resistance and antifouling performance than the other coatings did.
基金
This work was financially supported by the National Defense Science and Technology Key Laboratory Fund Project(61420050403)
the Young and Middle-aged Technology Innovation Leading Talents,and the Team Projects of Science and Technology Development Plan of Jilin Province(20230508041RC).