Air nanobubbles(A-NBs)were used to inhibit the brass corrosion in circulating cooling water for the first time in the study.The results of mass loss method and electrochemical method showed that A-NBs had the obvious corrosion inhibition effect.The inhibition rate reached 52%at 35℃.The impedance and surface characterization results of corrosion samples indicated that the corrosion inhibition mechanisms of A-NBs mainly included adsorption of corrosion ions,promoting the formation of the passivation film on metal surface and the formation of the bubble layer and scale film on metal surface.A-NBs are potential excellent corrosion inhibitors.