摘要
高级别连续油管产品的晶粒尺寸较小,采用传统的金相检验方法无法准确评定其晶粒度。利用金相检验和电子背散射衍射技术相结合的方法,对不同级别连续油管产品的晶粒尺寸进行研究。结果表明:采用电子背散射衍射技术能够准确评定高级别连续油管的晶粒尺寸,CT90连续油管的平均晶粒等积圆直径为2.89μm,CT110连续油管的平均晶粒等积圆直径为1.37μm。
The grain size of high-grade coiled tubing products was relatively small,and traditional metallographic testing methods could not accurately evaluate their grain size.Using a combination of metallographic examination and electron backscatter diffraction technology,the grain size of different grades of coiled tubing products was studied.The results show that using electron backscatter diffraction technology could accurately evaluate the grain size of high-level coiled tubing,and the average grain equicircle diameter of CT90 coiled tubing was 2.89μm.The average grain equicircle diameter of CT110 coiled tubing was 1.37μm.
作者
杨艳龙
周志超
赵乃胜
武甲
罗艺
YANG Yanlong;ZHOU Zhichao;ZHAO Naisheng;WU Jia;LUO Yi(Beijing Shougang Co.,Ltd.,Qian'an 064404,China)
出处
《理化检验(物理分册)》
CAS
2023年第11期4-6,共3页
Physical Testing and Chemical Analysis(Part A:Physical Testing)
关键词
连续油管
晶粒度
电子背散射衍射
显微组织
coiled tubing
grain size
electron backscatter diffraction
microstructure