Industrial-use VOx-based catalysts usually have a higher active temperature window (>250-300℃),which becomes a“bottleneck”for the practical application of PCDD/Fs catalytic degradation technology.In this work,VO_(x)-FeO_(x)/TiO_(2) catalyst prepared via mechanochemically method was investigated for the catalytic removal of PCDD/Fs.The removal efficiency of 1,2-DCBz,pure PCDD/Fs gas generated in the lab,PCDD/Fs from actual fue gas,long-term were studied,and the degradation mechanism was explored using FTIR and TOFMS.The degradation efficiency of 1,2-DCBz and PCDD/Fs on VO_(x)-FeO_(x)/TiO_(2) were higher than that of VO_(x)/TiO_(2)catalyst,and the optimal FeOx addition ratio was 3 wt.%.The characterization results show that the addition of FeOx can effectively improve the pore structure,surface acidity,and VOx dispersion of the catalyst,thus contributing to increasing the V^(5+)content and surface-active oxygen,which is conducive to the improvement of adsorption and redox performance of the catalyst.Under the actual MSWI (municipal solid waste incineration)fue gas,the PCDD/Fs removal efficiency over VTi-3Fe-MC maintained long-term stability,higher than 85%for 240 min.This result was not significantly reduced compared with the data obtained in the laboratory.According to the analysis results of intermediate products by FTIR and GC-TOFMS,it can be inferred that the epoxidation fracture of benzene ring is the rate-limiting step of dioxin catalytic degradation reaction.This work gives an in-depth view into the PCDD/Fs removal over VO_(x)-FeO_(x)/TiO_(2) catalysts and could provide guidelines for the rational design of reliable catalysts for industrial applications.
基金
supported by the Natural Science Foundation of Zhejiang Province (No. LY21E060007)
the National Natural Science Foundation of China (No. 52006191)。