摘要
Manganese(Mn)doped cadmium sulphide(Cd S)nanoparticles were synthesized using a chemical method.It was possible to decrease Cd S:Mn particle size by increasing Mn concentration.Investigation techniques such as ultraviolet-visible(UV-Vis)absorption spectroscopy and photoluminescence(PL)spectroscopy were used to determine optical properties of Cd S:Mn nanoparticles.Size quantization effect was observed in UV-Vis absorption spectra.Quantum efficiency for luminescence or the internal magnetic field strength was increased by doping Cd S nanoparticles with Mn element.Orange emission was observed at wavelength~630 nm due to ^(4)T_1→^(6)A_1 transition.Isolated Mn~(2+)ions arranged in tetrahedral coordination are mainly responsible for luminescence.Luminescence quenching and the effect of Mn doping on hyperfine interactions in the case of Cd S nanoparticles were also discussed.The corresponding weight percentage of Mn element actually incorporated in doping process was determined by atomic absorption spectroscopy(AAS).Crystallinity was checked and the average size of nanoparticles was estimated using the X-ray diffraction(XRD)technique.Cd S:Mn nanoparticles show ferromagnetism at room temperature.Transmission electron microscopy(TEM)images show spherical clusters of various sizes and selected area electron diffraction(SAED)patterns show the polycrystalline nature of the clusters.The electronic states of diluted magnetic semiconductors(DMS)ofⅡ-Ⅵgroup Cd S nanoparticles give them great potential for applications due to quantum confinement.In this study,experimental results and discussions on these aspects have been given.