摘要
采用多元醇法制备了直径约40 nm、长径比约300的银纳米线.以聚对苯二甲酸乙二醇酯-1,4-环己烷二甲醇酯(polyethylene terephthalateco-1,4-cylclohexylenedimethylene terephthalate,PETG)膜为基底,采用旋涂法制备了银纳米线柔性透明导电薄膜,探究了不同辅助成膜剂对成膜性能的影响.发现以黄原胶为辅助成膜剂制备的银纳米线薄膜具有较理想的透明性和导电性;银纳米线分散液沉积密度对银纳米线薄膜的透明性和导电性有重要影响,当沉积密度为10 mg/cm2时,银纳米线薄膜的透光率和导电性能最优;弯曲测试结果表明,银纳米线薄膜具有很好的柔韧性.
Silver nanowires with a diameter of approximately 40 nm and a length to diameter ratio of approximately 300 were prepared via the polyol method.Subsequently,uniform,stable,and exible transparent conductive lms of silver nanowires were prepared by the spin coating method.Polyethylene terephthalateco-1,4-cylclohexylenedimethylene terephthalate(PETG)lm was used as the substrate and Chitosan or Xanthan gum as the auxiliary lm forming agent.It was found that the deposition density of silver nanowires dispersion had an signi cant effect on the transparency and electrical conductivity of silver nanowires exible transparent conductive lms.The light transmittance and electrical conductivity of the lms reached a maximum when the deposition density was 10 mg/cm2.The bending performance test of the lm indicated good exibility.
作者
刘晓文
潜飞
张波
吴美莹
李红斌
张宝华
LIU Xiaowen;QIAN Fei;ZHANG Bo;WU Meiying;LI Hongbin;ZHANG Baohua(School of Environmental and Chemical Engineering,Shanghai University,Shanghai 200444,China;Taizhou Customs of People's Republic of China,Taizhou 318000,Zhejiang,China)
出处
《上海大学学报(自然科学版)》
CAS
CSCD
北大核心
2023年第6期1022-1029,共8页
Journal of Shanghai University:Natural Science Edition
基金
上海市教育基金会2016年度联盟计划资助项目(LM201667)。
关键词
多元醇法
银纳米线
旋涂法
柔性透明导电薄膜
polyol method
silver nanowires
spin coating method
exible transparent conductive lms