A novel Na_(1−x)K_(x)TaO_(3)perovskite microwave dielectric ceramic with high permittivity and high positive temperature coefficient

A novel Na_(1−x)K_(x)TaO_(3)(x=0,0.025,0.05,0.075,0.1,and 0.15)ceramic with high permittivity and high positive temperature coefficient was synthesized via the conventional solid-state method.All samples were determined to be pure phase orthorhombic NaTaO3 structure of space group Pmcn,and larger grain and lower porosity were observed after adding an appropriate amount of K+ions.The Q×f value is majored by the packing fraction and grain size,while the value ofτf is influenced by Ta–O bond valence.The Na_(0.95)K_(0.05)TaO_(3) ceramic possesses excellent dielectric properties ofεr=164.29,Q×f=9091 GHz(f=3.15 GHz),tanδ=3.46×10^(–4),τf=+809.52 ppm/℃,sintered at 1550℃.Compared with NaTaO_(3) ceramics,the Na_(1−x)K_(x)TaO_(3)ceramics prepared in this study demonstrate higher dielectric constants and higher positive temperature coefficients,which are promising for device miniaturization andτf compensators.