Influence of lanthanum on inclusions and as-cast microstructures in a low-alloy high-strength steel

原文传递
导出
摘要 Advanced high-strength steel ingots with total lanthanum(TLa)contents of 0,15×10^(–6),86×10^(–6)and 360×10^(–6)were prepared through laboratory experiments.The modification of inclusions and the variation of the as-cast microstructure with the content of lanthanum in the high-strength steel were analyzed.The result showed that with the increase in the TLa content in the steel from 0 to 360×10^(–6),the modification path of inclusions in the as-cast steel was Al2O_(3)and calcium aluminate→LaAlO_(3)→La_(2)O_(2)S→La_(2)O_(2)S–La2O_(3).The addition of La in the high-strength steel significantly refined the solidification structures.With the increase in the TLa content in the steel from 0 to 360×10^(–6),the ratio of the equiaxed crystal region in the macrostructure increased from 30.1%to 50.7%,the proportion of the high-angle grain boundary in the microstructure increased from 36.9%to 69.8%,and the area fraction of the acicular ferrite and the bainite increased from 0 to 93.3%.Inclusions of LaAlO_(3),La_(2)O_(2)S and La2O_(3)in the La-containing steel could act as heterogeneous nucleation cores ofα-Fe during the solidification.With the increase in the TLa content in the steel,the number density of inclusions that could act as effective heterogeneous nucleation cores in the steel gradually increased,which enlarged the ratio of the equiaxed crystal region and the proportion of intragranular acicular ferrite,and refined the as-cast microstructure of the high-strength steel.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2023年第12期2471-2481,共11页
基金 support from S&T Program of Hebei(Grant No.20311004D) the National Natural Science Foundation of China(Grant Nos.U22A20171 and 52104342) the Natural Science Foundation of Hebei Province(Grant No.E2021203062) the High Steel Center(HSC)at Yanshan University,Hebei Innovation Center of the Development and Application of High Quality Steel Materials,and Hebei International Research Center of Advanced and Intelligent Manufacturing of High Quality Steel Materials.
  • 相关文献

参考文献1

共引文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部