Design of novel RGO/2D strip-like ZIF-8/DMAOP ternary hybrid structure towards high-efficiency microwave absorption, active and passive anti-corrosion, and synergistic antibacterial performance

In order to meet the requirements of the marine environment for microwave absorption(MA)materials,we put forward the strategy of constructing multi-functional composite materials,which integrate microwave absorption,anti-corrosion,and antibacterial properties.Herein,graphene oxide(GO)was used as a template to induce the growth of zeolitic imidazolate framework-8(ZIF-8),simultaneously as a two-dimensional(2D)nanocontainers to load corrosion inhibitors to achieve pH-responsive and self-healing properties.Finally,quaternary ammonium salt(dimethyl octadecyl(3-trimethoxylsilyl propyl)ammonium chloride(DMAOP))and sodium ascorbate(VCNa)were introduced to achieve synergistic antibacterial activity and the reduction of GO.The 2D strip-like structure of ZIF-8 was due to the confined growth induced by the electrostatic attraction between ZIF-8 and GO sheets.The as-obtained reduced GO(RGO)/ZIF-8/DMAOP5 exhibited excellent microwave absorption(MA)properties,with a minimum reflection loss(RL)value of-47.08 dB at 12.73 GHz when the thickness was 2.8 mm.Moreover,the effective absorption bandwidth reached 6.84 GHz.After soaking in 3.5%NaCl solution for 35 days,the RGO/ZIF-8/DMAOP5-0.7%coating still achieved an impedance value of 4.585×107Ω·cm^(2) and a protective efficiency of 99.994%,providing superior anti-corrosion properties.In addition,fantastic antibacterial activity was obtained,with the antibacterial rates of RGO/ZIF-8/DMAOP_(10) reaching 99.39%and 100%against Escherichia coli and Staphylococcus aureus.This work could open new avenues towards the development of a new generation of multifunctional MA materials.