Ultra-high-temperature application of MXene: Stabilization of 2D Ti_(3)C_(2)T_(x) for cross-scale strengthening and toughening of 3D TiC

Transition metal carbide/nitride cores within MXenes make them considerably useful for ultra-high-temperature reinforcement.However,extensive research on Ti_(3)C_(2)T_(x) MXene has revealed its tendency to undergo a phase transition to TiCy at temperatures above 800℃due to high activity of a superficial Ti atomic layer.Herein,spark plasma sintering of Ti_(3)C_(2)T_(x) and TiC is performed to prevent the Ti_(3)C_(2)T_(x) phase transition at temperatures up to 1900℃through the fabrication of composites at a pressure of 50 MPa.Using a focused ion beam scanning electron microscope to separate layered substances in the composites and examining selected area diffraction spots in a transmission electron microscope enabled identification of non-phase-transitioned MXene.First-principles calculations based on density functional theory indicated the formation of strong chemical bonding interfaces between Ti_(3)C_(2)T_(x) and TiC,which imposed a stability constraint on the Ti atomic layer at the Ti_(3)C_(2)T_(x) surface.Mechanical performance tests,such as three-point bending and fracture toughness analysis,demonstrated that the addition of Ti_(3)C_(2)T_(x) can effectively improve the cross-scale strengthening and toughening of the TiC matrix,providing a new path for designing and developing two-dimensional(2D)carbides cross-scale-enhanced three-dimensional(3D)carbides with the same elements relying on a wide variety of MXenes.