摘要
研究液体1,4-聚丁二烯(LPB)在丁苯橡胶胶料中的应用。结果表明:LPB的微观结构主要为顺式-1,4-结构和反式-1,4-结构;采用LPB作为增塑剂替代环保芳烃油(TDAE),胶料的t10和t90延长,硫化胶的耐磨性能提高,滚动阻力降低,但同时抗湿滑性能下降;以LPB等量替代TDAE,硫化胶的拉伸性能下降,以LPB部分替代TDAE,硫化胶的拉伸性能提高。
The application of liquid 1,4-polybutadiene(LPB)in styrene butadiene rubber(SBR)compounds was studied.The results showed that the microstructure of LPB mainly consisted of cis-1,4-structure and trans-1,4-structure.Using LPB as a plasticizer to replace environmentally friendly aromatic oil(TDAE),the t10 and t90 of the compound were extended,the wear resistance of the vulcanizate increased,and the rolling resistance decreased,but at the same time,the wet slip resistance was reduced.Replacing TDAE with an equal amount of LPB resulted in a decrease in the tensile properties of the vulcanizate,while partially replacing TDAE with LPB resulted in an improvement in the tensile properties of the vulcanizate.
作者
王茜
张俊驰
吕贵杰
徐新圆
孙涛
刘恒
张春雨
孙宇
张学全
WANG Qian;ZHANG Junchi;LYU Guijie;XU Xinyuan;SUN Tao;LIU Heng;ZHANG Chunyu;SUN Yu;ZHANG Xuequan(Qingdao University of Science and Technology,Qingdao 266042,China)
出处
《橡胶工业》
CAS
2024年第4期266-270,共5页
China Rubber Industry
基金
国家自然科学基金青年科学基金资助项目(52103116)。